PA0101-LR010717CONCRETE COMPRESSIVE STRENGTH TEST
8901 Carpenter Fn~'., Suite #100
Report Number: 94011093.0022 Dallas, Texas 75247
Service Date: July 6, 2001 (214) 63O-lOlO
Client: City of Coppell - Parks & Recreation Re July 17, 2001
Attn: Brad Reid t: Andrew Brown Park East
732 DeForest Moore Road
Coppell TX 75019 Coppell, Texas
Pr .~ct Number: 94011093
Material Information Informatio~
Specified Strength: 3000 psi @ 28 Days Sam Date Cast: July 6, 2001
Technician: Eric Garcia
Batch Time: 7:54am Plant: 31 Weather Conditions: Partly cloudy, sunny
Supplier: TXI Accumulative Yards: 70
Truck No: 737 Ticket No: 2931097 Placement Method: Pump
Mix I.D. No.: 8272 Sample Locations: See placement location
Placement Location: Paving on plaza area between softball
fields on E side of park
(See attached sketch)
Field Test Data
Test Result Specification Test Method
Slump, inches: 4.00 3-5 ASTM C-143
Air Content, %: 3-6
Concrete Temperature, o F: 89 ASTM C-1064
Ambient Temperature, o F: 81 ASTM C-1064
Plastic Unit Weight, pcf:
Laboratory Test Data Age at Maximum Compressive
Set Specimen Diameter Area Date Test Load Strength
No. ID (inches) (.sq. inches) Tested (days) (lbs) (psi)
1 1 6.00 28.27 07/13/2001 7 72,820 2,570
1 2 6.00 28.27 07/13/2001 7 77,950 2,760
Ave rage 2,670
1 3 08/03/2001 28
1 4 08/03/2001 28
Services - Obtain samples of fresh concrete at the placement locations, perform required field tests and cast compressive
strength samples.
ASTM C-31, C-39, C-172, C-1231 01~I
1-zo
Technician: Eric Ga re ia
Report Distribution:
(1) city of coppell - Parks & Recreation Reviewed by:
(1) TLB Construction v ~'~r~. Cleveland, P.E.
(1) City of Coppell - Constr. Insp.
Senior Project Engineer
The tests were performed in general accordance with applicable ASTM, AASHTO, or DOT test methods. This report is exclusively for the use of the client
indicated above and shall not be reproduced except in full without the written approval of Terracon. Test results transmitted herein are only applicable
to the actual samples tested at the location(s) referenced and are not necessarily indicative of the properties of other apparently similar or identical
materials.
Page 1 of 1