Deforest Court-LR020509 (2)CONCRETE COMPRESSIVE STRENGTH TEST
Report Number: 94021148.0010
Service Date: May 1, 2002
Client: The Holmes Builders
Attn: Jon Doster~Dean Trudell
1406 Halsey Way Suite 100
Carroliton TX 75007
8901 Carpenter Frwy., Suite #100
Dallas, Texas 75247
(214) 630'1010
pR~j~,~...~. May 09, 2002
616 DeForest Court
[ *' Single Family Home~
PrOject N-'E~ber: 94021148
Materfal Information
Specified Strength: 3000 psi (~ 28 Days
Batch Time: 9:33am
Supplier:. Redi-Mix
Truck No: 203
Mix I.D. No.: 914MR
Plant: 1
Ticket No: 17728
Sample Information
sample Time: 10:45am Date Cast: May 1, 2002
Technician: Steve Campbell
Weather Conditions: Clear
Accumulative Yards: 10
PlaCement Method: Direct Discharge
Sample Locations: Pier 23
Placement Location: Piers 19, 23, 30, 38, 39
Field Test Data
Test Result Specification
Slump, inches: 6.00 5-7 ASTM C-143
Air Content, %: N/A
Concrete Temperature, o F: 88 ASTM C1064
Ambient Temperature, o F: 84 ASTM C-1064
Plastic Unit Weight, pcf:
Laboratory Test Data
Age at
Set Specimen Diameter Area Date Test
No. ID (inches) (sq. inches.) Tested (days)
I 1 6.00 28.27 05/08/2002 7
I 2 6.00 28.27 05/0812002 7
1 3
1 4
Test Method
05~29/2002
Maximum Compressive
Load Strength
(lbs) (psi)
65,270 2,310
62,930 2,230
Average 2,270
28
05/29/2002 28
Services - Obtain samples of fresh concrete at the plaCement locations, perform required field tests and cast compressive
strength samples.
Technician: Steve Campbell ~ ~' / 7
Report Distribution: HBC Engineering
(1) The Holmes Builders
(1) City of Coflpell - Constr Insp ~ Reviewed by:
(1) Clly of Coppell- Bldg Insp Hussain H. Abusaad, P.E.
Senior Project Manager
The tests were pe~ormed in general accordance with applicable ASTM, AASH~rO, or DOT test ~. This reix~t is e~'olusively for ltne use of the Client
indicated above and shell r~ he reproduced excep~ in full without the written approval of Terraco~. Test results transmitted herein are o~ly appitcab~e
to the actual samples tested at the location(s) referenced and are not necessarily indicative of the proi)erfles of offnar apparently similar or identical
materials.
Page I of I