Deforest Court-LR020517Field Test Data
Test
Slump, inches:
Air Content,
CONCRETE COMPRESSIVE S(NGTH TEST
Report Number: 94021129.0010
Service Date: April 18, 2002
Client: The Holmes Builders
Attn: Dennis Ward
1406 Halsey Way Suite 100
Carrollton TX 75007
Material Information
Specified Strength: 3000 psi 28 Days
Batch Time: 4:15pm
Supplier. Redi -Mix
Truck No: 217
Mix I.D. No.: 914
Concrete Temperature, F:
Ambient Temperature, o F:
Plastic Unit Weight, pcf:
Laboratory Test Data
1 3
1 4
Technician: Phil Green
Report Distribution:
(1) The Holmes Builders
(1) City of Coppell Constr Insp
(1) City of Coppell Bldg lnsp
Plant: 1
Result
4.00
1.7
87
85
Set Specimen Diameter Area
No. ID (inches) (sq. inches)
1 1 6.00 28.27
1 2 6.00 28.27
6.00 28.27
6.00 28.27
Ticket No: 17343
Report Date: M
Project:
Specification
5 -7
N/A
Page 1 of 1
Project s '21129
Age at Maximum
Test Load
(days) (Ibs)
7 75,350
7 73,740
Average
05/16/2002 28 107,500
05/16/2002 28 112,290
Average
Date
Tested
04/25/2002
04/25/2002
Reviewed by:
Test Method
ASTM C -143
ASTM C -231
ASTM C1064
ASTM C -1064
a.dI■ke. aJ$ucram,
ENGINEERING
8901 Carpenter Frwy., Suite #100
Dallas, Texas 75247
(214)630.1010
Sample information
Sample Time: 5:15pm Date Cast:April 18, 2002
Technician: Phil Green
Weather Conditions: Cloudy, warm
Accumulative Yards: 30
Placement Method: Crane Bucket
Sample Locations: Pier #23
Placement Location: Piers
Compressive
Strength
(Psi)
2,660
2,610
2,640
3,800
3,970
3,890
Services Obtain samples of fresh concrete at the placement locations, perform required field tests and cast compressive
strength samples.
HBC Engineering
Hussein H. Abusaad, P.E.
Senior Project Manager
The tests were performed in general accordance with applicable ASTM, AASHTO, or DOT test methods. This report is exclusively for the use of the client
indicated above and shall not be reproduced except in full without the written approval of Terracon. Test results transmitted herein are only applicable
to the actual samples tested at the location(s) referenced and are not necessarily indicative of the properties of other apparently similar or Identical
materials.