Amberpoint BP-LR020606CONCRETE COMPRESSIVE STRENGTH TEST
Report Number: 94021029.0291
Service Date: May 29, 2002
Client: Transwestern Commercial Services
Attn: Jim Gaspard
5001 Spring Valley Rd. Suite 600W
Dallas TX 75244
8901 Carpenter Frwy., Suite #100
Dallas, Texas 75247
(214) 630-1010
Repo~fe: J"~ne 06, 2002
ProjeCt: Amberpoint Buildin~No. 1
~@ Coppell
~'Ol~n~rexas
Project Number: 94021029
Material Information
Specified Strength: 3000 psi @ 28 Days
Batch Time: 9:22am
Supplier: Hanson
Truck No: 1031
Mix I.D. No.: 9373
Plant: 22
Ticket No: 52792
Sample Information
Sample Time: 11:55am Date Cast: May 29, 2002
Technician: Brad Rengstorff
Weather Conditions: Clear
Accumulative Yards: 5
Placement Method: Direct Discharge
Sample Locations: See placement location
Placement Location: Pier Hole Q/2.8
Field Test Data
Test Result Specification
Slump, inches: 4.25 5-7
Air Content, %: 1.3 N/A
Concrete Temperature,o F: 89
76
Ambient Temperature, o F:
Laboratory Test Data
Set Specimen Diameter Area Date
1 1 6.00 28.27 06/01/2002 3
1 2 6.00 28.27 06/05/2002 7
I 3 06/26/2002 28
1 4 06/26/2002 28
Test Method
ASTM C-143
ASTM C-231
ASTM C1064
ASTM C-1064
Age at
Maximum Compressive
Test Load Strength
(days) (lbs) (psi)
88,560 3,130
119,380 4,220
NOTE:
Concrete placed was over two (2) hours old.
Services - Obtain samples of fresh concrete at the placement locations, perform required field tests and cast compressive
strength samples.
Technician: Brad Rengstorff
Report Distribution:
(1) Transweatern Commercial Services
(1) O'Bden & Associates Inc
(1) TechniStructures Inc
(1) City of Coppell - Constr Insp
(1) City of Coppell - Bldg Insp
(1) Hill & Wilkinson Ltd
(1) Halff Associates
(1) State Farm Insurance
Reviewed by:
HBC Engine,~
Eugene Harbour
The tests were performed in general accordance with applicable ASTM, AASHTO, or DOT test methods. This report is exclusively fo~ the use of the cfient
indicated above and shall not be reproduced except in full without the written approval of Terracon. Test results transmitted herein are only applicable
to the actual samples tested at the location(s) referenced and are not necessarily indicative of the properties of other apparently similar o~ identical
materials.
Page 1 of 1