Valley R Plaza 2B-LR030701CONCRETE COMPRESSIVE STRENGTH TEST IBC
Report Number: lrerracon
(
Service Date: June 3, 2003 Dail Carpenter F Ste #100
Dallas, Texas 75247 47
(214) 630 -1010
Client: Phase II BLMA Limited Report Date: July 01, 2003
Attn: Tad Weatherford Project: Valley Ranch Plaza Phase II
5950 Berkshire Ln Ste 410 817 South MacArthur Blvd
Dallas TX 75225 Coppell, TX
Project Number: 94031170
Material Information
Specified Strength: 4000 psi @ 28 Days
Batch Time:
12:36pm
Supplier:
Redi -Mix
Truck No:
111
Mix I.D. No.:
723
Field Test Data
Test
Slump, inches:
Air Content, %:
Plant: 1
Sample Information
Sample Time: 2:00pm Date Cast: June 3, 2003
Technician: Josh Sherman
Weather Conditions: Clear, hot
Ticket No: 110513 Placement Method: Direct Discharge
Sample Locations:
Placement Location: Inlet box, NE corner
Result Specification Test Method
ASTM C -143
Concrete Temperature, 0 F:
93
ASTM C -1064
Ambient Temperature, ° F:
91
ASTM C -1064
Plastic Unit Weight, pcf:
Laboratory Test Data
Age at Maximum
Compressive
Set Specimen Diameter
Area
Date
Test Load
Strength
No. ID (inches) ( sq.
inches
Tested
(days) (lbs)
(psi)
1 1 6.00
28.27
06/10/2003
7 111,220
3,930
1 2 6.00
28.27
06/10/2003
7 104,260
3,690
Average
3,810
1 3 6.00
28.27
07/01/2003
28 126,960
4,490
1 4 6.00
28.27
07/01/2003
28 133,980
4,740
Average
4,620
Comments: Not tested for plastic unit weight.
Services - Obtain samples of fresh concrete at the placement locations, perform required field tests and cast compressive
strength samples.
Technician: Josh Sherman
Report Distribution: / ,IWgely4con
(1) Phase II BLMA Limited /, // L/
(1) City of Coppell TX Reviewed by y y
(1) City of Coppell TX Eric J. Cleveland, P.E.
Senior Project Engineer
The tests were performed in general accordance with applicable ASTM, AASHTO, or DOT test methods. This report is exclusively for the use of the client
indicated above and shall not be reproduced except in full without the written approval of Terracon. Test results transmitted herein are only applicable
to the actual samples tested at the location(s) referenced and are not necessarily indicative of the properties of other apparently similar or identical
materials.
Pace 1 of 1 01 LLWM 1 F- Kw