Four Seasons 2R-LR050406CONCRETE COMPRESSIVE STRENGTH TEST
Report Number: 94041388.0095
Service Date: March 31, 2005
lr'erracan
8901 Carpenter Fnvy, Ste #100
Dallas, Texas 75247
(214) 630-1010
Client: Hill & Wilkinson LTD
Attn: Charles Hoagland
800 Klein Rd Ste 100
Piano TX 75074
Report Date: April 06, 2005
Project: BCE Specialties
989 West Sandy Lake Road
Coppell, TX
Project Number: 94041388
Material Information
Specified Strength: 4000 psi @ 28 Days
Batch Time:
Supplier:
Truck No:
Mix I.D. No.:
Ticket No:
Sample Information
sample Time: Date Cast: March 25, 2005
Technician: Contractor Made
Weather Conditions:
Placement Method:
Sample Locations: See Placement Location
Placement Location: Grate Inlets, Sta. 3+14, Royal Lane at Pro.
Line Inlet #2
Field Test Data
Test Result Specification Test Method
Slump, inches: ASTM C143
Air Content, %: ASTM C231
Concrete Temperature, o F: ASTM C1064
Ambient Temperature, o F: ASTM C1064
Plastic Unit Weight, pcf: ASTM C138
Laboratort/ Test Data
Age at Maximum Compressive
Set Specimen Diameter Area Date Test Load Strength
No. ID (inches) (sq. inches) Tested (days) (lbs) (psi)
1 1 6.00 28.27 04/05/2005 11 101,930 3,600
1 2 6.00 28.27 04/05/2005 11 103,320 3,650
Average 3,630
1 3 04/22/2005 28
1 4' 04/22/2005 28
Comments: Not tested for plastic unit weight.
Services - Pick up test cylinders cast by others and return them to the laboratory for curing and testing.
Technician: Chris Eubanks
(1) Hill & Wilkinson LTD (1) City of Coppell TX
(1) Hardy McCullah/MLM Architects ~nc (1) BCE Specialties Reviewed by:
(1) TMBP Consulting Engineers
(1) City of Coppell TX
a ers nio P 'i
The tests were performed in general accordance with applicable ASTM, AASHTO, or DOT test methods. This report is exclusively for the use of the client
indicated above and shah not be reproduced except in full without the written consent of our company. Test results transmitted herein are only applicable
to the actual samples tested at the location(s) referenced and are not necessarily indicative of the properties of other apparently similar or identical
materials.