Coppell Trade-LR051221CONCRETE COMPRESSIVE STRENGTH TEST
Report Number: 94051190.0161
Service Date: November 22, 2005
'lrerracon
8901 Carpenter Finny, Ste #100
Dallas, Texas 75247
(214) 630-1010
Client: ~
Coppell Trade~7~ter LP
Attn: Benne~atliff
5055 Kelle?'Spdngs Rd Ste 300
Addison TX 75001
Material Information
Specified Strength: 4000 psi ~ 28 Days
Batch Time: 8:00am
Supplier: TXI
Truck No: 805
Mix I.D. No.: 8602
Field Test Data
Test
Plant: 141 ~
Ticket No: 160333
Slump, inches:
Air Content, %:
Concrete Temperature,O F:
Ambient Temperature, o F:
Plastic Unit Weight, pcf:
Laboratory Test Data
set Specimen Diameter Area
No. ID (inches) (sq. inches)
1 1 6.00 28.27
Report Date: December 21,2005
Project: Coppell Trade Center - Bldg C
NWC Sandy Lake/Freeport Pkwy
Coppell, TX
Project No.: 94051190
Sample Information
Sample Time: 9:1 lam Date Cast: November 22, 2005
Technician: Daniel J. Dregos
Weather Conditions:Cool and sunny
Accumulative Yards: 30
Placement Method: Direct Discharge
Sample Locations: Sidewalk, W side at F/24
Placement Location: Building C, W side Entrances at Column
Line F/13, F/19 and F/24
Result / IS_oecificaLion
65
46
Test Method
ASTM C143
ASTM C231
ASTM C1064
ASTM Cl 064
ASTM C138
Age at Maximum Compressive
Date Test Load Strength
Tested (days) (lbs) (psi)
11/29/2005 7 114,300 4,040
1 2 6.00 28.27 12/20/2005 28 156,480 5,530
1 3 6.00 28.27 12/20/2005 28 150,420 5,320
Average 5,430
1 4 01/17/2006 56
Comments: Not tested for plastic unit weight.
Services - Obtain samples of fresh concrete at the placement locations, perform required field tests and cast compressive
strength samples.
Technician: Daniel J. Dregos
(1) TechniStruclures (1) McFadden&Mgler Revlewea Dy. ~',/~---~ ~ v ~"~ .~' ,/ ../'
(1) City of Coppell TX (1) Macatee Engineering Inc ~ Robert D. Ray, S.E.T~J
(1) C~ty of Coppell TX Senior Project Mayn't~
The tests were performed in general accordance with applicable ASTM, AASHTO, or DOT test methods. This report is exclusively for the use o/the client'
indicated above and shall not be reproduced except in full without the written consent of our company. Test results transmitted herein are only applicable
to the actual samples tested at the location(s) referenced and are not necessarily indicative of the properties of other apparently similar or identical
materials.