Coppell Trade-LR060209CONCRETE COMPRESSIVE STRENGTH TEST
Report Number: 94051190.0206
Service Date: February 1,2006
" rl !frEIcon
8901 Carpenter FnNy, Ste #100
Dallas, Texas 75247
(214) 630-1010
Client:
Coppell Trade Center LP
Attn: Bennet Ratliff
5055 Keller Springs Rd Ste 300
Addison TX 75001
Report Date: February 09,
Project: coppell Trade Center - Bldg,.,,,,~
~ NWC SanclT~ ,'F,,-~rt Pkwy
Coppell, TX
Project No.: 94051190
Material Information
Specified Strength: 4000 psi ~ 28 Days
Batch Time: 6:37am Plant: 141
Supplier: TXI
Truck No: 834 Ticket No: 198007
Mix I.D. No.: 8206
Water Added Onsite Before Test: 15 Gallons
Water Added Onsite After Test: 5 Gallons
Field Test Data
Test
Result
Slump, inches: 5.00
Air Content, %: 4.2
Concrete Temperature,o F: 64
Ambient Temperature, o F: 56
Plastic Unit Weight, pcf: 146.0
Laboratory Test Data
set Specimen Diameter Area
No. ID (inches) (sq. inches)
Sample Information
Date Cast: February 1,2006 Time:7:30am
Technician: Polikarp J. Labecki
Weather ConditionsCIoudy
Accumulative Yards: 10/30
Placement Method: Direct Discharge
Sample Locations: Dock#2
Placement Location:Pavement, Loading Docks: #2, #3, ¢/4 & #5
Docks from SW Building
Specification
Date
Tested
Test Method
ASTM C143
ASTM C231
ASTM C1064
ASTM C1064
ASTM C138
Age at Maximum Compressive
Test Load Strength
(days) (lbs) (psi)
1 1 6.00 2827 02/04/2006 3 114,910 4,060
1 2 6.00 28.27 02/08/2006 7 126,550 4,480
1 3 6.00 28.27 02/08/2006 7 128,230 4,530
Average 4,510
1 4 03/01/2006 28
1 5 03/01/2006 28
Services - Obtain samples of fresh concrete at the placement locations, perform required field tests and cast compressive
strength samples.
Technician: Polikarp J. Labecki
Report Distribution:
(1) Coppell Trade Center LP
(1) TechniStructures
(1) City of Coppell TX
(1) City of Coppell TX
(1) Mol nan Asset lnc
(1) McF Jden & Miller Reviewed by:.¢~(.~d_.--/(/'~z-~ '~ /
(1) Mac ee Engineering Inc ¢,- Robert D. Ray, ~
S e nior P roj~l~ra.n.,a g er ,,
The tests were performed in general accordance with applicable ASTM, AASHTO, or DOT test methods. This report is exclusively for the use or the client
indicated above and shall not be reproduced except in full without the written consent of our company. Test results transmitted herein are only applicable
to the actual samples tested at the location(s) referenced and are not necessarily indicative of the properties of other apparently similar or identical
materials.